INVESTIGATING PB-INDUCED STRESS CORROSION CRACKING OF ALLOY 800 VIA IN- SITU XPS

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:International Conference on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (19. : 2019 : Boston, Mass.) 19th International Conference on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors 2019 ; Volume 2 of 2
1. Verfasser: Payne, B. (VerfasserIn)
Weitere Verfasser: Persaud, S. Y. (VerfasserIn), Smith, J. M. (VerfasserIn)
Pages:19
Format: UnknownFormat
Sprache:eng
Veröffentlicht: 2020
Schlagworte:
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Titel Jahr Verfasser
ON THE POTENTIAL SYNERGIES OF HELIUM AND HYDROGEN ON THE NUCLEATION AND STABILITY OF CAVITY CLUSTERS IN INCONEL X-750 30 IRRADIATED IN A HIGH THERMAL NEUTRON FLUX SPECTRA 2020 Judge, C. D.
OXIDATION CHARACTERISTICS OF NI-CR-FE ALLOY SYSTEMS IN SIMULATED PWR PRIMARY WATER: EFFECT OF CR CONTENT 2020 Hur, H. S. Shim. D. H.
SMALL SCALE TENSILE TESTING OF GRAIN BOUNDARY STRENGTH OF X-750 ALLOY 2020 He, L.
THE INFLUENCE OF METAL SUBSTRATE ON CRUD BUILD-UP UNDER SIMULATED PWR CONDITIONS 2020 Cassineri, S.
COUPLING EFFECT OF CHARGED-HYDROGEN AND COLD WORK ON OXIDATION BEHAVIOR OF 316L STAINLESS STEEL IN DEAERATED HIGH TEMPERATURE WATER 2020 Cui, T.
INTER-DIGITAL CAPACITIVE SENSOR FOR EVALUATING CABLE INSULATION THROUGH JACKET 2020 Glass, S. W.
EVALUATION OF THE INFLUENCE OF IRRADIATION DOSE RATE ON CRACK GROWTH BEHAVIOR OF IRRADIATION ASSISTED STRESS CORROSION CRACKING FOR NEUTRON- IRRADIATED STAINLESS STEELS IN HIGH-TEMPERATURE WATER OF A BOILING WATER REACTOR 2020 Koshiishi, M.
TRIBOCORROSION PHENOMENA IN CO- AND FE-BASED HARDFACING ALLOYS EVALUATED USING PIN-IN-ON-DISC WEAR TESTS IN A SIMULATED PWR ENVIRONMENT 2020 Ratia, V. L.
EFFECT OF MARTENSITE ON SCC INITIATION IN AUSTENTITC STAINLESS STEELS IN SIMULATED PWR PRIMARY WATER ENVIRONMENT 2020 Chang, L.
THE EFFECT OF IRRADIATION-INDUCED MATRIX BARRIER HARDENING ON IRRADIATION-ASSISTED STRESS CORROSION CRACKING (IASCC) IN AUSTENITIC STEELS AND NICKEL BASED ALLOYS 2020 Faulkner, R. G.
HIGH TEMPERATURE CYCLIC DEFORMATION BEHAVIOR OF AN ADVANCED B AUSTENITIC STAINLESS STEEL (ALLOY 709) 2020 Alsmadi, Z. Y.
CORROSION PERFORMANCE OF SUPERAUSTENTIC STAINLESS STEEL AL-6XN IN HIGH TEMPERATURE WATER 2020 Stiger, M. J.
PHYSICALLY-BASED MODELING OF ENVIRONMENTAL FATIGUE CRACK GROWTH IN TYPE 304/304L STAINLESS STEEL 2020 Anglin, B. S.
UNDERSTANDING THE EVOLUTION OF DEFORMATION STRUCTURES AT FATIGUE CRACK TIPS AND IMPLICATIONS FOR ENVIRONMENTALLY ENHANCED AND RETARDED FATIGUE CRACK GROWTH 2020 Miller, B. D.
ELECTROCHEMICAL BEHAVIOUR OF DILUTE ELECTROACTIVE SPECIES ON A HEAT- TRANSFER SURFACE UNDER BOILING 2020 Dever, C.
ENVIRONMENTALLY-ASSISTED SHORT CRACK FATIGUE TESTING ON AUSTENITIC STAINLESS STEELS 2020 Coult, B. E.
INFLUENCE OF MEAN STRESS AND PWR ENVIRONMENT ON FATIGUE BEHAVIOR OF A 304L SS 2020 Peng, Z.
IRRADIATION-ASSISTED STRESS CORROSION CRACKING OF TI-STABILIZED AUSTENITIC STAINLESS STEEL 2020 Ernestova, M.
USE OF ON-LINE MONITORING TECHNIQUES FOR EVALUATIONS OF LEAD STRESS CORROSION CRACKING (PBSCC) AND A PBSCC INHIBITOR 2020 Capell, B.
INFLUENCE OF HEAT TRANSFER CREVICE CONDITIONS ON STRESS CORROSION CRACKING IN LEAD FAULTED ALKALINE ENVIRONMENS 2020 Miller, F. D.
Alle Artikel auflisten