Experimental study of corrosion-induced degradation of reinforced concrete elements

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	International RILEM Conference on Materials, Systems and Structures in Civil Engineering (2016 : Lyngby-Tårbaek) International RILEM Conference on Materials, Systems and Structures in Civil Engineering 2016 - Segment on service life of cement-based materials and structures ; Vol. 1
1. Verfasser:	Loukil, Olfa (VerfasserIn)
Weitere Verfasser:	Adelaide, Lucas (VerfasserIn), Bouteiller, Véronique (VerfasserIn), Quiertant, Marc (VerfasserIn), Chaussadent, Thierry (VerfasserIn), Raguenau, Frédéric (VerfasserIn), Bourbon, Xavier (VerfasserIn), Trenty, Laurent (VerfasserIn)
Pages:	2016 -
Format:	UnknownFormat
Sprache:	eng
Veröffentlicht:	2016
Schlagworte:
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Bestellen

Titel	Jahr	Verfasser
Some examples on shrinkage restraint effects on concrete and concrete structures	2016	Benboudjema, Farid
Computational prediction of restraint-induced macrocrack patterns in concrete walls	2016	Knoppik-Wróbel, Agnieszka
Experimental study of corrosion-induced degradation of reinforced concrete elements	2016	Loukil, Olfa
Carbon nanoparticles cement-based materials for service life monitoring	2016	Monteiro, André O.
Water release process of superabsorbent polymers in cement paste at early age	2016	Wang, Yujiang
Influence of fibre reinforcement on the initiation of corrosion-induced cracks	2016	Berrocal, Carlos G.
Experimental investigation on strain distribution in reinforcement of RC specimens under tension loading	2016	Kaklauskas, Gintaris
Couplings between creep and damage: Role of the fracture criterion	2016	Dunant, Cyrille
Service life prediction of a cementitious coating system based on chloride-induced corrosion	2016	Dong, Hua
Impact of slag content in alkali-activated slag cement on porosity of concrete	2016	Krivenko, Pavel
Control of early age cracking in a massive tunnel structure based on experimental investigations and numerical simulations	2016	Hermerschmidt, Wibke
Residual concrete strength after sustained load: Experimental results and modelling approach	2016	Kammouna, Zainab
Coupling limit states of corrosion initiation and corrosion induced crack opening - sensitivity analysis of model parameters	2016	Ferreira, Miguel
Numerical simulation since early ages of the RG8 beam test from concrack benchmark by means of a 3D fibre frame model	2016	Crespo, Maria D.
Properties of concrete recycling clay-rich dredging sediments as a novel supplementary cementitious material	2016	Bunderen, Céline Van
Developing an engineering approach for migrating from prescriptive to performance-based specification for concrete	2016	Nanukuttan, Sreejith
Usability of basalt fibres in fibre reinforced cementitious composites	2016	Girgin, Zehra Canan
Concrete drying: effects of boundary conditions and specimen shape	2016	Carette, Jéróme
Mitigation of early age shrinkage of UHPFRC by using spent equilibrium catalyst	2016	Matos, Ana Mafalda
Volume stability of alkali activated Portland cement concretes with alkali-susceptible aggregates	2016	Krivenko, Pavel

Alle Artikel auflisten