DEVELOPMENT OF A GASEOUS IODINE TESTING SYSTEM TO DETERMINE THE I-SCC PROPERTIES OF ZIRCONIUM ALLOYS

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:International Conference on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (19. : 2019 : Boston, Mass.) 19th International Conference on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors 2019 ; Volume 1 of 2
1. Verfasser: Hanlon, S. M. (VerfasserIn)
Weitere Verfasser: Phillion, A. (VerfasserIn), Gillen, C. (VerfasserIn), Daymond, M. R. (VerfasserIn)
Pages:19
Format: UnknownFormat
Sprache:eng
Veröffentlicht: 2020
Schlagworte:
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Titel Jahr Verfasser
CHARACTERIZATION OF MICROSTRUCTURE OF ALLOY 52M WELD METAL NEAR THE FUSION BOUNDARY AND OXIDE FILMS FORMED IN SIMULATED PWR PRIMARY WATER 2020 Zhang, K.
SCC OF ALLOY 82 WELD METAL 2020 Andresen, P. L.
DEVELOPMENT AND VALIDATION OF A NEW EXPERIMENTAL DEVICE FOR STUDIES OF IODINE STRESS CORROSION CRACKING OF ZIRCONIUM ALLOYS 2020 Wilezynska, K.
SCC BEHAVIOR AT ALLOY 52M-182 WELD OVERLAY INTERFACES IN A PWR ENVIRONMENT 2020 Alexandreanu, B.
REVEALING HOW ALKALI CATIONS AFFECT THE ELECTRICAL DOUBLE LAYER A STRUCTURE OF STAINLESS STEEL IN ALKALINE AQUEOUS ENVIRONMENTS 2020 Giron, R. G. P.
CONCURRENT EFFECTS OF IRRADIATION AND HYDROGENATION ON MICROSTRUCTURAL AND MECHANICAL PROPERTIES OF ZR BASED FUEL CLADDING ALLOYS 2020 Kano, S.
TECHNICAL BASIS FOR ASME SECTION XI CODE CASE FOR STRESS CORROSION CRACK GROWTH RATE EVALUATIONS FOR ALLOY 690 AND ASSOCIATED WELDS 2020 Bamford, W.
ENVIRONMENTALLY ASSISTED CRACKING AND FRACTURE TOUGHNESS OF AN IRRADIATED STAINLESS STEEL WELD 2020 Chen, Y.
FRACTURE PROPERTY DEGRADATION IN CAST STAINLESS STEELS AFTER LONG-TERM THERMAL AGING 2020 Byun, T. S.
ENVIRONMENTAL DEGRADATION RESISTANCE OF ATF FECRAL CLADDING TUBE SPECIMENS DURING THE FUEL CYCLE 2020 Schuster, M.
CRACK INITIATION BEHAVIOR OF COLD-WORKED ALLOY 690 IN SIMULATED PWR PRIMARY WATER - ROLE OF STARTING MICROSTRUCTURE, APPLIED STRESS AND COLD WORK ON PRECURSOR DAMAGE EVOLUTION 2020 Zhai, Z.
CHARACTERIZATION OF IN-SERVICE THERMAL AGING EFFECTS IN BASE METALS AND WELDS OF THE PRESSURE VESSEL OF A DECOMMISSIONED PWR PRESSURIZER, AFTER 27 YEARS OF OPERATION 2020 Joly, P.
STRESS CORROSION CRACKING OF AN AUSTENITIC STAINLESS STEEL PIPE WELD 2020 Ickes, M:R.
OPERATIONAL EXPERIENCE OF SIEMENS/KWU LWR NUCLEAR POWER PLANTS 2020 Kilian, R.
DEVELOPMENT OF PREDICTION METHOD FOR RADIATION HARDENING OF REACTOR INTERNALS 2020 Seto, H.
MICROSTRUCTURAL CHARACTERIZATION OF PROTON IRRADIATED 304L SS AT 100°C AND 360°C 2020 Judge, C. D.
EFFECT OF MATERIAL CONDITION ON STRESS CORROSION CRACK INITIATION OF COLD-WORKED ALLOY 600 IN SIMULATED PWR PRIMARY WATER . 2020 Zhai, Z.
DISTINCT EFFECTS OF IRRADIATION ON THE STRUCTURE AND CHEMICAL REACTIVITY OF SILICATES AND CARBONATES 2020 Plante, E. C. La
EFFECT OF GAMMA IRRADIATION ON CREEP PROPERTIES OF CEMENT PASTE ANALOGUES 2020 Rodriguez, E. T.
RADIATION-INDUCED FERRITE FORMATION AS A POTENTIAL ISSUE IN PWR AUSTENITIC INTERNALS FOLLOWING PLANT LIFE EXTENSION 2020 Merezhko, D. A.
Alle Artikel auflisten